Less splishy, splashy mixing of the different alloys in the mold when cast?ĭo we really need to stay at the 1/3 soft alloy to 2/3 hard alloy ratio. How about pre-casting soft noses to the final hunting molds nose size? They could be brought up to slump temperature in the mold on a hot plate and the mold would be hot enough to cast with a harder alloy. 311" round ball at 45gr for 30 cals? Soft nose weight consistency would be better. Instead of floating the mold on the melt, why not use the hot plate and set the temperature to what you want?Ĭan I cast say, a Lee 356-100-1R or 356-120-TC from pure lead to use for the 310gr. Thinking hard on Bruce B's soft point method today.